Desenvolvimento e caracterização de scaffolds laminar para regeneração de tecido cartilaginoso traqueal
| dc.contributor.advisor | Chaud, Marco Vinícius | |
| dc.contributor.author | Amaral, Venâncio Alves | |
| dc.date.accessioned | 2023-05-09T20:57:25Z | |
| dc.date.available | 2023-05-09T20:57:25Z | |
| dc.date.issued | 2017 | |
| dc.description.abstract | INTRODUÇÃO: O processamento tecnológico de polímeros naturais e sintéticos tem sido estudado para fabricação de dispositivos tridimensionais porosos, comumente denominados de scaffolds. OBJETIVO: Desenvolver e caracterizar scaffolds laminar, para aplicação na regeneração de tecido cartilaginoso traqueal. MÉTODOS: Os scaffolds foram preparados com poli (L-co-D,L ácido lático) (PLDLA), polietilenoglicol (PEG) 400 e 4000 e com agente porogênico, sacarose (SAC) e colágeno (COL). Preparados na proporção 1:2:2 (m/m) pela técnica de evaporação de solvente. As formulações foram avaliadas quanto as estruturas de superfície por microscopia óptica, propriedades físico-químicas por espectroscopia de infravermelho com transformada de Fourier (FTIR) e calorimetria diferencial exploratória (DSC), as propriedades fisiomecânicas foram medidas pela resistência a tração, compressão e mucoadesão, e no estudo in vitro, foram avaliados o perfil de desintegração e intumescimento em três diferentes meios (água ultrapura, meio tamponado e fluído salivar simulado-FSS) e avaliados até 120 horas. Após essas análises, as formulações PLDLA/PEG400/SAC e PLDLA/PEG400/COL foram selecionadas, e seguiram para análise de microscopia eletrônica de varredura, microtomografia computadorizada e ensaio de viabilidade celular. RESULTADOS: As micrografias exibiram alteração na estrutura de superfície com formação de poros. Os espectros de FTIR com os termogramas de DSC sugerem interação química entre os componentes dos scaffolds. Os resultados apresentados nas propriedades fisiomecânicas, de uma forma geral, mostraram que os scaffolds com PEG 400 e COL são favoráveis para o uso traqueal. O perfil de desintegração apresentou inicialmente uma perda de massa para todos os scaffolds, sendo menor para as que continham COL. Em contrapartida, os perfis de intumescimento para estas amostras foram maiores. O scaffold PLDLA/PEG400/SAC apresentou porosidade de 63,25% após 120h em FSS. Já o scaffold PLDLA/PEG400/COL apresentou porosidade de 58,97% após 120h em FSS. Os ensaios de viabilidade celular mostraram que os scaffolds não são citotóxicos. CONCLUSÃO: As análises dos resultados apresentados indicam que ambas as composições PLDLA/PEG400/SAC e PLDLA/PEG400/COL são estruturalmente adequados para serem utilizados na regeneração de tecido cartilaginoso. | por |
| dc.description.abstract | INTRODUCTION: The technological processing of natural and synthetic polymers has been studied for the manufacture of porous three-dimensional devices, commonly known as scaffolds. OBJECTIVE: To develop and characterize laminar scaffolds for application in the regeneration of tracheal cartilage tissue. METHODS: The scaffolds were prepared with poly (L-co-D, L lactic acid) (PLDLA), polyethylene glycol (PEG) 400 and 4000 and with porogenic agent, being sucrose (SUC) and collagen (COL). Prepared in the ratio 1:2:2 (w/w) by the solvent evaporation technique. The formulations were evaluated for surface structures by optical microscopy, physicochemical properties by Fourier Transform Infrared Spectroscopy (FTIR) and Differential Scanning Calorimetry (DSC), the physiomechanical properties were measured by tensile strength, compression and mucoadhesion, and in the in vitro study, the disintegration and swelling profile in three different media (ultrapure water, buffered medium and salivary fluid simulated-SFS) were evaluated and evaluated up to 120 hours. After these analyzes, the PLDLA/PEG400/SAC and PLDLA/PEG400/COL formulations were selected and followed for scanning electron microscopy, computerized microtomography and cell viability assay. RESULTS: The micrographs showed alterations in the surface structure with pore formation. The FTIR spectra with the DSC thermograms suggest chemical interaction between scaffold components. The results presented in the physiological properties generally showed that scaffolds with PEG 400 and COL are favorable for tracheal use. The disintegration profile initially presented a loss of mass for all scaffolds, being smaller for those containing COL. In contrast, the swelling profiles for these samples were higher. The scaffold PLDLA/PEG400/SAC had porosity of 63.25% after 120h in SFS. The scaffold PLDLA/PEG400/COL had porosity of 58.97% after 120h in SFS. Cell viability assays have shown that the scaffolds are no cytotoxic. CONCLUSION: Analyzes of the results indicated that both PLDLA/PEG400/SAC and PLDLA/PEG400/COL compositions are structurally suitable for use in the regeneration of cartilaginous tissue. | eng |
| dc.identifier.uri | https://repositorio.uniso.br/handle/uniso/833 | |
| dc.subject | Materiais biomédicos | |
| dc.subject | Tecidos (Anatomia e fisiologia) | |
| dc.subject | Engenharia biomédica | |
| dc.title | Desenvolvimento e caracterização de scaffolds laminar para regeneração de tecido cartilaginoso traqueal | |
| dc.type | Dissertação | |
| dspace.entity.type | Publication | |
| local.rights | Open Access | |
| relation.isAdvisorOfPublication | abae6895-ebe7-4205-be96-2b9225d56eae | |
| relation.isAdvisorOfPublication.latestForDiscovery | abae6895-ebe7-4205-be96-2b9225d56eae |
Arquivos
Pacote Original
1 - 1 de 1